electronic silicone potting compound HM-955
Key:electronic silicone potting compound,two compounds water-proof potting silicone sealants for LED, electrically insulating potting compound ​​​
Characteristic: electronic silicone potting compound,two compounds water-proof potting silicone sealants for LED, electrically insulating potting compound ​​​ixing A,B parts according to proportion A:B=10:1 on the basis of weight or volume until evenly. Suggest to stir A and B part resp…
Hotline:0086-757-82711390
        Introduction

electronic silicone potting compound,two compounds water-proof potting silicone sealants for LED,
electrically insulating potting compound


 

HOMEEN is a leading silicone sealant manufacturer ,we mainly produce neutral one component electronic silicone sealant for consumer electronics ,for example ,conduction cooker ,oven ,fridge ,iron,etc .

We also produce two component potting compound for LED power driver ,and potting compound for LED display .

HOMEEN provide whole solution for LED ,solar PV ,consumer electronic ,automobile ,craft ,etc .



Potting compound for LED power driver

HM-955 instructions

Features

Curing at room temperature, heat to accelerate curing.

Solvent-free and no accessory substance, vey low shrinkage

Remarkable thermal-conducting and dielectric property.

Operating temperature range -50C~250C

properties

product

HM-955

 

A

B

color

white

black

Mixed ratio

1

1

viscosity/mPa·s

2000-2500

3500-4000

Specific gravity

1.55

Curing time

4-5h/28C1h/80C

Operation time

40-60min/25C

Shore Hardness /A

55-60

Dissipation factor

0.003

Shrinkage percentage %

0.3-0.5

Flame retardant rating

UL94-V1

Dielectric constant

3.0

Volume resistivity/Ω·cm

1015

Tensile strength/Mpa

1.5

Elongation at break/%

84

Dielectric strength/kV/mm

18

Thermal conductivity/W/m/K

0.7~0.9

Waterproof Rating

IP65

Note: This product is subject to curing temperature, the  temperature is higher, the operation and full curing time will be shorter.

workmanship

Mixing A,B parts according to proportion A:B=10:1 on the basis of weight or volume until evenly. Suggest to stir A and B part respectively before mixing them to make it uniform distribution. Then dispense the adhesive on the potting position. If need high-thermal conductivity vacuum  deaeration

 is necessary otherwise no need. It can be cured at room temperature or by heating. But it is featured of room temperature curing, there is summertime and wintertime types, the two types are sthe same except for the operation time.

Note:

This silicon rubber is vulcanized by platinum catalys, the nitrogen, sulfur, phoshor and rgano-tin compound material may hinder its vulcanization, so please clean the rosin on the PCB and use the soldering tin with low lead content.

Packaging:40kg/set

Storage period :sealed under 30C, the A,B parts shelf life are 9 nine months after production. Thereare sediments come after 3 months,please mix it thorough eveness before using.

$n-8;: 88 0%;font-family:宋体;mso-ascii-font-family: "Times New Roman";mso-hansi-font-family:"Times New Roman";mso-bidi-font-family: 宋体;mso-font-kerning:0pt'>·s


2000-2500

3500-4000

Specific gravity

1.55

Curing time

4-5h/28C1h/80C

Operation time

40-60min/25C

Shore Hardness /A

55-60

Dissipation factor

0.003

Shrinkage percentage %

0.3-0.5

Flame retardant rating

UL94-V1

Dielectric constant

3.0

Volume resistivity/Ω·cm

1015

Tensile strength/Mpa

1.5

Elongation at break/%

84

Dielectric strength/kV/mm

18

Thermal conductivity/W/m/K

0.7~0.9

Waterproof Rating

IP65

Note: This product is subject to curing temperature, the  temperature is higher, the operation and full curing time will be shorter.

workmanship

Mixing A,B parts according to proportion A:B=10:1 on the basis of weight or volume until evenly. Suggest to stir A and B part respectively before mixing them to make it uniform distribution. Then dispense the adhesive on the potting position. If need high-thermal conductivity vacuum  deaeration

 is necessary otherwise no need. It can be cured at room temperature or by heating. But it is featured of room temperature curing, there is summertime and wintertime types, the two types are sthe same except for the operation time.

Note:

This silicon rubber is vulcanized by platinum catalys, the nitrogen, sulfur, phoshor and rgano-tin compound material may hinder its vulcanization, so please clean the rosin on the PCB and use the soldering tin with low lead content.

Packaging:40kg/set

Storage period :sealed under 30C, the A,B parts shelf life are 9 nine months after production. Thereare sediments come after 3 months,please mix it thorough eveness before using.

 

 

 


Recommended
silicone cookware handle
stainless steel cookware handle
diecasting pan handle
cookware handles for pan and pot ​
cookware handle, cookware parts
Contact HOMEEN
silicone bakeware,cookware parts and silicone sealant supplier
Tel:0086-757-82711390
Fax:0086-757-82711390
E-mail:marketing1@hm-sil.com
Add:Lianhua Development Zone,Dinghu District,Zhaoqing City,Guangdong,China.